Grain Structure, Crystallographic Texture, and Hardening Behavior of Dissimilar Friction Stir Welded AA5083-O and AA5754-H14

Author:

Ahmed Mohamed Mohamed ZakyORCID,Ataya SabbahORCID,Seleman Mohamed Mohamed El-SayedORCID,Allam TarekORCID,Alsaleh Naser AbdulrahmanORCID,Ahmed EssamORCID

Abstract

This work investigated the effect of friction stir welding (FSW) tool rotation rate and welding speed on the grain structure evolution in the nugget zone through the thickness of the 10 mm thick AA5083/AA5754 weldments. Three joints were produced at different combinations of FSW parameters. The grain structure and texture were investigated using electron backscattering diffraction (EBSD). In addition, both the hardness and tensile properties were investigated. It was found that the grain size varied through the thickness in the nugget (NG), which was reduced from the top to the base in all welds. Reducing the rotation rate from 600 rpm to 400 rpm at a constant welding speed of 60 mm/min reduced the average grain size from 33 µm to 25 µm at the top and from 19 µm to 12 µm at the base. On the other hand, the increase of the welding speed from 20 mm/min to 60 mm/min had no obvious effect on the average grain size. This implied that the rotation rate was more effective in grain size reduction than the welding speed. The texture was the mainly simple shear texture that required some rotations to obtain the ideal simple shear texture. The hardness distribution, mapped for the nugget zone, and the parent alloys indicated a diffused softened welding zone. The heating effect of the pressure and rotation of the pin shoulder and the heat input parameter (ω/v) on the hardness value of the nugget zone were dominating. Tensile stress-strain curves of the base alloys and that of the FSWed joints were evaluated and presented. Moreover, the true stress-true strain curves were determined and described by the empirical formula after Ludwik, and then the materials strengthening parameters were determined. The tensile specimens of the welded joint at a revolution speed of 400 rpm and travel speed of 60 mm/min possessed the highest strain hardening parameter (n = 0.494).

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3