Structural, Magnetic, Dielectric and Piezoelectric Properties of Multiferroic PbTi1−xFexO3−δ Ceramics

Abstract

PbTi1−xFexO3−δ (x = 0, 0.3, 0.5, and 0.7) ceramics were prepared using the classical solid-state reaction method. The investigated system presented properties that were derived from composition, microstructure, and oxygen deficiency. The phase investigations indicated that all of the samples were well crystallized, and the formation of a cubic structure with small traces of impurities was promoted, in addition to a tetragonal structure, as Fe3+ concentration increased. The scanning electron microscopy (SEM) images for PbTi1−xFexO3−δ ceramics revealed microstructures that were inhomogeneous with an intergranular porosity. The dielectric permittivity increased systematically with Fe3+ concentration, increasing up to x = 0.7. A complex impedance analysis revealed the presence of multiple semicircles in the spectra, demonstrating a local electrical inhomogeneity due the different microstructures and amounts of oxygen vacancies distributed within the sample. The increase of the substitution with Fe3+ ions onto Ti4+ sites led to the improvement of the magnetic properties due to the gradual increase in the interactions between Fe3+ ions, which were mediated by the presence of oxygen vacancies. The PbTi1−xFexO3−δ became a multifunctional system with reasonable dielectric, piezoelectric, and magnetic characteristics, making it suitable for application in magnetoelectric devices.