FTIR Monitoring of Polyurethane Foams Derived from Acid-Liquefied and Base-Liquefied Polyols

Abstract

Polyalcohol liquefaction can be performed by acid or base catalysis, producing polyols with different properties. This study compared the mechanical properties of foams produced using polyols from liquefied Cytisus scoparius obtained by acid and base catalysis and using two different foam catalysts. The differences were monitored using FTIR analysis. Acid-catalyzed liquefaction yielded 95.1%, with the resultant polyol having an OH index of 1081 mg KOH/g, while base catalysis yielded 82.5%, with a similar OH index of 1070 mg KOH/g. Generally, compressive strength with dibutyltin dilaurate (DBTDL) ranged from 16 to 31 kPa (acid-liquefied polyol) and 12 to 21 kPa (base-liquefied polyol), while with stannous octoate (TIN), it ranged from 17 to 42 kPa (acid) and 29 to 68 kPa (base). Increasing water content generally decreased the compressive modulus and strength of the foams. Higher water content led to a higher absorption at 1670 cm−1 in the FTIR spectrum due to the formation of urea. Higher isocyanate indices generally improved compressive strength, but high amounts led to unreacted isocyanate that could be seen by a higher absorption at 2265 cm−1 and 3290 cm−1. DBTL was shown to be the best foam catalyst due to higher trimer conversion seen in the spectra by a higher absorption at 1410 cm−1. Acid- and base-derived polyols lead to different polyurethane foams with different FTIR spectra, particularly with a higher absorption at 1670 cm−1 for foams from acid-derived liquefaction.