Effect of Salt Solution Environment on the Aging of Styrene−Butadiene−Styrene (SBS)-Modified Asphalt

Abstract

The aim of this paper is to investigate the aging mechanism of asphalt in the sea salt erosion environment from a rheological point of view. In order to simulate the real pavement aging process in the sea salt erosion environment, base asphalt and Styrene−Butadiene−Styrene (SBS)-modified asphalt were selected for salt environment aging tests. The asphalt samples were aged via a thin film oven test (TFOT) and a pressure aging vessel (PAV) test. Then, thermo-oxidizing conditions were created after the samples were immersed in salt solution, mixed with four different concentrations of sodium chloride (NaCl) and sodium sulphate (Na2SO4), to investigate the aging state of asphalt. Temperature scan (TS), frequency scan (FS), and multiple stress creep and recovery (MSCR) tests performed using a Dynamic Shear Rheometer (DSR) were used to investigate the effects on the rheological properties of aged asphalt in a salt environment. The results showed that both base asphalt and SBS-modified asphalt were aged to different degrees under mixed salt solutions. The two asphalt samples aged in a salt environment showed increased hardness. SBS-modified asphalt exhibited higher aging resistance compared with base asphalt in the sea salt environment. However, due to the degradation of the SBS modifier and the aging of base asphalt, the properties of the SBS-modified asphalt showed more obvious complexity with changes in salt solution concentrations.