Development of a Chitosan/PVA/TiO2 Nanocomposite for Application as a Solid Polymeric Electrolyte in Fuel Cells

Author:

Ruiz Gómez Elio Enrique,Mina Hernández José HerminsulORCID,Diosa Astaiza Jesús Evelio

Abstract

The influence of the incorporation of nanoparticles of titanium oxide (TiO2) at a concentration between 1000 and 50,000 ppm on the physicochemical and mechanical properties of a polymer matrix formed from a binary mixture of chitosan (CS) and polyvinyl alcohol (PVA) at a ratio of 80:20 and the possibility of its use as a solid polymeric electrolyte were evaluated. With the mixture of the precursors, a membrane was formed with the solvent evaporation technique (casting). It was found that the incorporation of the nanoparticles affected the moisture absorption of the material; the samples with the highest concentrations displayed predominantly hydrophobic behavior, while the samples with the lowest content displayed absorption values of 90%. Additionally, thermogravimetric analysis (TGA) showed relatively low dehydration in the materials that contained low concentrations of filler; moreover, differential scanning calorimetry (DSC) showed that the nanoparticles did not significantly affect the thermal transitions (Tg and Tm) of the compound. The ionic conductivity of the compound with a relatively low concentration of 1000 ppm TiO2 nanoparticles was determined by complex impedance spectroscopy. The membranes doped with a 4 M KOH solution demonstrated an increase in conductivity of two orders of magnitude, reaching values of 10−6 S·cm−1 at room temperature in previously dried samples, compared to that of the undoped samples, while their activation energy was reduced by 50% with respect to that of the undoped samples. The voltage–current test in a proton exchange membrane fuel cell (PEMFC) indicated an energy efficiency of 17% and an open circuit voltage of 1.0 V for the undoped compound, and these results were comparable to those obtained for the commercial membrane product Nafion® 117 in evaluations performed under conditions of 90% moisture saturation. However, the tests indicated a low current density in the undoped compound.

Publisher

MDPI AG

Subject

Polymers and Plastics,General Chemistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3