Modelling of Fatigue Delamination Growth and Prediction of Residual Tensile Strength of Thermoplastic Coupons

Abstract

Thermoplastic composites are continuously replacing thermosetting composites in lightweight structures. However, the accomplished work on the fatigue behavior of thermoplastics is quite limited. In the present work, we propose a numerical modeling approach for simulating fatigue delamination growth and predicting the residual tensile strength of quasi-isotropic TC 1225 LM PAEK thermoplastic coupons. The approach was supported and validated by tension and fatigue (non-interrupted and interrupted) tests. Fatigue delamination growth was simulated using a mixed-mode fatigue crack growth model, which was based on the cohesive zone modeling method. Quasi-static tension analyses on pristine and fatigued coupons were performed using a progressive damage model. These analyses were implemented using a set of Hashin-type strain-based failure criteria and a damage mechanics-based material property degradation module. Utilizing the fatigue model, we accurately foretold the expansion of delamination concerning the cycle count across all interfaces. The results agree well with C-scan images taken on fatigued coupons during interruptions of fatigue tests. An unequal and unsymmetric delamination growth was predicted due to the quasi-isotropic layup. Moreover, the combined models capture the decrease in the residual tensile strength of the coupons. During the quasi-static tension analysis of the fatigued coupons, we observed that the primary driving failure mechanisms were the rapid spread of existing delamination and the consequential severe matrix cracking.