Author:
Ke Qingjin,Dai Feilong,Li Shengxi,Rong Maohua,Yao Qingrong,Wang Jiang
Abstract
Phase formation and microstructure of (Nd1-2xCexYx)14.5Fe79.3B6.2 (x = 0.05, 0.10, 0.15, 0.20, 0.25) alloys were studied experimentally. The results reveal that (Nd1-2xCexYx)14.5Fe79.3B6.2 annealed alloys show (NdCeY)2Fe14B phase with the tetragonal Nd2Fe14B-typed structure (space group P42/mnm) and rich-RE (α-Nd) phase, while (Nd1-2xCexYx)14.5Fe79.3B6.2 ribbons prepared by melt-spun technology are composed of (NdCeY)2Fe14B phase, α-Nd phase and α-Fe phase, except for the ribbon with x = 0.25, which consists of additional CeFe2 phase. On the other hand, magnetic properties of (Nd1-2xCexYx)14.5Fe79.3B6.2 melt-spun ribbons were measured by a vibrating sample magnetometer (VSM). The measured results show that the remanence (Br) and the coercivity (Hcj) of the melt-spun ribbons decrease with the increase of Ce and Y substitutions, while the maximum magnetic energy product ((BH)max) of the ribbons decreases and then increases. The tendency of magnetic properties of the ribbons could result from the co-substitution of Ce and Y for Nd in Nd2Fe14B phase and different phase constitutions. It was found that the Hcj of the ribbon with x = 0.20 is relatively high to be 9.01 kOe, while the (BH)max of the ribbon with x = 0.25 still reaches to be 9.06 MGOe. It suggests that magnetic properties of Nd-Fe-B ribbons with Ce and Y co-substitution could be tunable through alloy composition and phase formation to fabricate novel Nd-Fe-B magnets with low costs and high performance.
Funder
National Natural Science Foundation of China
Subject
General Materials Science
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献