3–5, 8–14 μm mid-far infrared (MF-IR) coherent lights generated by nonlinear optical (NLO) crystals are crucial for many industrial and military applications. AgGaGe5Se12 (AGGSe) is a promising NLO candidate because of its good optical performance. In this paper, the large AGGSe single crystal of 35 mm diameter and 80 mm length was obtained by the seed-aided Bridgman method. The crystalline quality was characterized with X-ray diffraction, rocking curve, transmission spectrum. The FWHM of the (210) peak was about 0.05° and the IR transmission was about 60% (1–10 μm, 6 mm thick). Additionally, it performed well in 8 μm frequency doubling, with a maximum output power of about 41 mW, corresponding to an optical-to-optical conversion efficiency of 3.2%. The laser induced damage threshold (LIDT) value was about 200 MW/cm2 (1.06 μm, 20 ns, 1 Hz).
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献