Abstract
The optical photoluminescent (PL) emission of Yb3+ ions in the near infrared (NIR) spectral region at about 950–1100 nm has many potential applications, from photovoltaics to lasers and visual devices. However, due to their simple energy-level structure, Yb3+ ions cannot directly absorb UV or visible light, putting serious limits on their use as light emitters. In this paper we describe a broadband and efficient strategy for sensitizing Yb3+ ions by Ag codoping, resulting in a strong 980 nm PL emission under UV and violet-blue light excitation. Yb-doped silica–zirconia–soda glass–ceramic films were synthesized by sol-gel and dip-coating, followed by annealing at 1000 °C. Ag was then introduced by ion-exchange in a molten salt bath for 1 h at 350 °C. Different post-exchange annealing temperatures for 1 h in air at 380 °C and 430 °C were compared to investigate the possibility of migration/aggregation of the metal ions. Studies of composition showed about 1–2 wt% Ag in the exchanged samples, not modified by annealing. Structural analysis reported the stabilization of cubic zirconia by Yb-doping. Optical measurements showed that, in particular for the highest annealing temperature of 430 °C, the potential improvement of the material’s quality, which would increase the PL emission, is less relevant than Ag-aggregation, which decreases the sensitizers number, resulting in a net reduction of the PL intensity. However, all the Ag-exchanged samples showed a broadband Yb3+ sensitization by energy transfer from Ag aggregates, clearly attested by a broad photoluminescence excitation spectra after Ag-exchange, paving the way for applications in various fields, such as solar cells and NIR-emitting devices.
Funder
Ministero degli Affari Esteri e della Cooperazione Internazionale
VINNOVA
Knut och Alice Wallenbergs Stiftelse
Horizon 2020 Framework Programme
Istituto Nazionale di Fisica Nucleare
Subject
Fluid Flow and Transfer Processes,Computer Science Applications,Process Chemistry and Technology,General Engineering,Instrumentation,General Materials Science
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献