Ion-Enhanced Etching Characteristics of sp2-Rich Hydrogenated Amorphous Carbons in CF4 Plasmas and O2 Plasmas

Abstract

The sp2-rich hydrogenated amorphous carbon (a-C:H) is widely adopted as hard masks in semiconductor-device fabrication processes. The ion-enhanced etch characteristics of sp2-rich a-C:H films on ion density and ion energy were investigated in CF4 plasmas and O2 plasmas in this work. The etch rate of sp2-rich a-C:H films in O2 plasmas increased linearly with ion density when no bias power was applied, while the fluorocarbon deposition was observed in CF4 plasmas instead of etching without bias power. The etch rate was found to be dependent on the half-order curve of ion energy in both CF4 plasmas and O2 plasmas when bias power was applied. An ion-enhanced etching model was suggested to fit the etch rates of a-C:H in CF4 plasmas and O2 plasmas. Then, the etch yield and the threshold energy for etching were determined based on this model from experimental etch rates in CF4 plasma and O2 plasma. The etch yield of 3.45 was observed in CF4 plasmas, while 12.3 was obtained in O2 plasmas, owing to the high reactivity of O radicals with carbon atoms. The threshold energy of 12 eV for a-C:H etching was obtained in O2 plasmas, while the high threshold energy of 156 eV was observed in CF4 plasmas. This high threshold energy is attributed to the formation of a fluorocarbon layer that protects the a-C:H films from ion-enhanced etching.