AbstractInjection molding products made of aluminum flakes and polymer blends exhibit a distinctive esthetic effect. However, during the filling process, the melt flows in different directions converge and collide, resulting in the flop effect of the aluminum flake and consequent weld line formation. Herein, microcellular injection molding (MIM) was employed to fabricate polypropylene/aluminum flakes (PP/Al) composite foamed parts with distinct weld lines using supercritical nitrogen (scN2) as the physical blowing agent. The scN2 content has a significant effect on cell diameter and cell density. When the scN2 content was 0.6%, the weld line width of the foamed part was 13.03 μm, while it was 30.41 μm for the solid counterpart due to the expansion and rupture of cells in the flow front during filling. Moreover, the orientation of Al flakes was mostly along the flow direction for the foamed parts, while it was generally aligned perpendicular to the flow direction for solid parts in the weld line region. In addition, the flexural modulus of foamed parts was increased by 29% compared with the solid parts, although the tensile strength was reduced by 18% due to the alignment of Al flakes and the stress concentration on the cell walls. Therefore, this work provides insight into the improvement of flexural property and the mitigation of weld lines for injection molded composite parts using MIM.
Funder
National Natural Science Foundation of China
Subject
Materials Chemistry,Polymers and Plastics,Surfaces, Coatings and Films,General Chemistry
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献