Preparation and characterization of CNTs/CaCu3Ti4O12/silicone rubber composites with improved dielectric and mechanical properties

Author:

Zeng Yu1ORCID,Tang Lu1,Li Guijin2

Affiliation:

1. The Center of Collaboration and Innovation Jiangxi University of Technology Nanchang China

2. Intelligent Manufacturing Department Jiangxi University of Technology Nanchang China

Abstract

AbstractThe dielectric performance of Silicone rubber (SR) composites can be significantly enhanced by carbon nanotubes. However, carbon nanotubes are easy to agglomerate in the polymer matrix. Adding low‐dimensional materials of different dimensions may be a solution. In this article, one‐dimensional multiwall carbon nanotubes (CNTs) and zero‐dimensional copper calcium titanate (CaCu3Ti4O12, CCTO) ceramic fillers were simultaneously added to prepare silicone dielectric elastomer composites. SEM results showed that the CNTs were distributed uniformly in the SR matrix due to the addition of CCTO. When 2 wt% CNTs and 10 wt% CCTO were added, the dielectric constant of the composite increased from 2.79 (pure silicone rubber) to 5.72, with a low loss tangent of 0.0012. Due to the uniform dispersion of CNTs with the addition of CCTO particles, dielectric performance of the composites were enhanced. The tensile stress was 986 kPa, the elongation at break was 333%, while the elastic modulus was not more than 613 kPa (2 wt% CNTs and 5 wt% CCTO in the SR composite). In addition, the composites had a wide temperature range up to 400°C. Therefore, the prepared CNTs/CCTO/SR composites have good dielectric and mechanical properties, and good thermal stability. It has a good reference value for this kind of composites as dielectric elastomer materials.

Publisher

Wiley

Subject

Materials Chemistry,Polymers and Plastics,Surfaces, Coatings and Films,General Chemistry

Cited by 3 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3