Effect of nano‐silica on fatigue behavior of glass fiber‐reinforced epoxy composite laminates: A Weibull distribution approach

Author:

Gupta Akash1,Singh Manjeet1ORCID,Saini J. S.2ORCID

Affiliation:

1. School of Mechanical Engineering Lovely Professional University Phagwara Punjab India

2. Mechanical Engineering Department Thapar Institute of Engineering and Technology Patiala Punjab India

Abstract

AbstractThe aim of this study is to assess the impact of nano‐silica in glass fiber‐reinforced epoxy composite (GFEC) subjected to static and fatigue loading. Laminates were prepared in compression molding machine followed by the tensile test and tension‐tension fatigue testing at five different stress levels (from 50% to 90% of ultimate tensile strength). The addition of 3 wt% of nano‐silica with epoxy improved the tensile and fatigue strength as compared to neat GFEC. Scanning electron microscope (SEM) images of the fractured specimen showed the damage pattern which indicates that neat GFEC laminate exhibited damage patterns characterized by fiber breakage and matrix cracking. On the other hand, the modified GFEC with nano‐silica showed damage patterns including fiber pullout accompanied by fiber breakage and matrix cracking. During cyclic loading, the stress–strain hysteresis loop shows a reduced slope, indicating a decrease in the dynamic modulus of the specimen. This reduction in slope signifies a loss of stiffness during cyclic loading, particularly at high‐stress levels. The highest dynamic modulus at high‐stress levels indicates a rapid progression of severe damage and a shorter fatigue life. On the other hand, at low‐stress levels, the lower magnitude of dynamic modulus suggests a moderate damage progression and a longer fatigue life.Highlights Effect of nano‐silica in GFEC under static and fatigue loading conditions. GFEC with 3 wt% of nano‐silica shows improved tensile and fatigue strength. Examination of damage patterns through SEM analysis of the fractured surface. Depiction of the failure modes using damage pattern under fatigue loading. Comparison of fatigue life and dynamic modulus for neat and modified GFEC.

Publisher

Wiley

Subject

Materials Chemistry,Polymers and Plastics,General Chemistry,Ceramics and Composites

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3