Improvement of Orange II Photobleaching by Moderate Ga3+Doping of Titania and Detrimental Effect of Structural Disorder on Ga Overloading

Abstract

Highly photoactive Ga3+-doped anatase modification of titania was prepared by homogeneous hydrolysis of aqueous solutions mixture of titanium oxo-sulphate TiOSO4and gallium(III) nitrate with urea. Incorporation of Ga3+into the anatase lattice has a clear positive effect on the photocatalytic activity under UV and Vis light irradiation up to a certain extent of Ga. Ga3+doping decreased the size of the crystallites, increased surface area, and affected texture of the samples. Higher amount of gallium leads to the formation of a nondiffractive phase, probably photocatalytically inactive. The titania sample with 2.18 wt.% Ge3+had the highest activity during the photocatalysed degradation in the UV and visible light regions; the total bleaching of dye Orange II was achieved within 29 minutes. Ga concentration larger than 5% (up to 15%) significantly inhibited the growth of the anatase crystal domains which formed the nondiffractive phase content and led to remarkable worsening of the photobleaching efficiency.