Fabrication and Characterization of In Situ Synthesized SiC/Al Composites by Combustion Synthesis and Hot Press Consolidation Method

Abstract

The in situ SiC/Al composites were fabricated in Al-Si-C systems with different Si/C mass ratios and holding time by the method of combustion synthesis and hot press consolidation. The influences of Si/C mass ratio and holding time on the phase constitution, microstructure, and hardness of the composites were investigated. The results indicate that the increase of Si/C mass ratio leads to more uniform size distribution of the SiC particles in the Al matrix. Moreover, by improving the Si/C mass ratio from 4 : 1 to 5 : 1, the maximum size of SiC particle was reduced from 4.1 μm to 2.0 μm. Meanwhile, the percentage of submicroparticles was increased from 22% to 63%, and the average hardness value of the composites was increased by 13%. In addition, when the holding time is set to be fifteen minutes, the Al4C3 phase did not exist in the composites because of its total reactions with Si atoms to form SiC particles, and the average hardness value was 73.8 HB.