EBSD patterns simulating multilayer twins based on dynamical theory of electron diffraction

Abstract

AbstractElectron backscatter diffraction (EBSD) can be employed to determine crystal structures but has not been used alone to identify defects at the atom scale due to the lack of understanding of the EBSD patterns generated by various structure defects. In the present work, the EBSD patterns of FCC‐Fe with 9‐layer, 6‐layer and 3‐layer twin structures are simulated, respectively, using the revised real space (RRS) method and compared with the counterpart of perfect crystals. Our results show that when the electron beam is incident along a direction parallel to the twin plane, the pattern appears symmetrical with respect to the corresponding Kikuchi band of the twin plane, and the diffraction details within the Kikuchi band also exhibit symmetry with respect to the middle line of the Kikuchi band. Moreover, the overall clarity of the patterns decreases, and the pattern becomes more blurred with increasing the distance from the Kikuchi band corresponding to the twin plane. By contrast, the incident electron beam along the direction perpendicular to the twin plane results in diffraction superposition of the matrix region and the shear region, which shows twofold rotational symmetry with respect to the Kikuchi pole corresponding to the normal to the twin plane. In addition, some extra Kikuchi bands appear in the EBSD patterns due to the long‐period structures of the multilayer twins. As the number of multilayer twins decreases, the number of extra Kikuchi bands decreases and the area of the blurring pattern increases. The correlation between twin structures and EBSD patterns provides theoretical insights for identifying twin structures by the EBSD technique.