Thermal fatigue of single-crystalline superalloy CMSX-4®: a comparison of epitaxial laser-deposited material with the base single crystal-Reference-Cited by-同舟云学术

Thermal fatigue of single-crystalline superalloy CMSX-4®: a comparison of epitaxial laser-deposited material with the base single crystal

Published:2001-02 Issue:1-2 Volume:299 Page:152-156
ISSN:0921-5093
Container-title:Materials Science and Engineering: A
language:en
Short-container-title:Materials Science and Engineering: A

Author:

Felberbaum L,Voisey K,Gäumann M,Viguier B,Mortensen A

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Reference7 articles.

1. Epitaxial laser metal forming: analysis of microstructure formation

2. Superalloys, Seven Springs Mountain Resort, Champion, PA, USA;Harris,1992

3. F. Meyer-Olbersleben, Thermische Ermüdung Einkristalliner Nickelbasis-Legierungen, Ph.D. thesis #1255, Ecole Polytechnique Fédérale de Lausanne, Switzerland, 1994.

4. M.R. Blümm, Einfluss der Anisotropie auf das thermische Ermüdungsverhalten von Nickelbasis-Legierungen, Ph.D. thesis #1460, Ecole Polytechnique Fédérale de Lausanne, Switzerland, 1995.

Cited by 41 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Thermal fatigue behavior of the ZGH451 Ni-based superalloy fabricated by direct energy deposition in the temperature range of 900–1100 °C;Journal of Materials Science & Technology;2025-03

2. Fracture failure analysis of DZ125 directionally solidified superalloy under combined high and low cycle fatigue;Engineering Fracture Mechanics;2024-11

3. High-temperature thermal fatigue of Ni3Al-based single crystal alloy affected by wall thickness and peak temperature;Journal of Materials Research and Technology;2024-07

4. A Study of the Internal Deformation Fields and the Related Microstructure Evolution during Thermal Fatigue Tests of a Single-Crystal Ni-Base Superalloy;Materials;2024-06-10

5. Thermal fatigue failure analysis and life assessment of Ni-based single crystal superalloys with film cooling holes;Engineering Fracture Mechanics;2024-05