Reliability analysis of fatigue crack growth for rail steel under variable amplitude service loading conditions and wear-Reference-Cited by-同舟云学术

登录注册会员服务联系我们

Reliability analysis of fatigue crack growth for rail steel under variable amplitude service loading conditions and wear

Published:2021-11 Issue: Volume:152 Page:106450
ISSN:0142-1123
Container-title:International Journal of Fatigue
language:en
Short-container-title:International Journal of Fatigue

Author:

Masoudi Nejad Reza,Liu Zhiliang,Ma Wenchen,Berto Filippo

Funder

National Natural Science Foundation of China

University of Electronic Science and Technology of China

Publisher

Elsevier BV

Subject

Industrial and Manufacturing Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,Modeling and Simulation

Reference57 articles.

1. Three-dimensional simulation of rolling contact fatigue crack growth in UIC60 rails;Masoudi Nejad;Tribol Trans,2016

2. Mechanics of a fatigue crack nucleation mechanism;Lin;J Mech Phys Solids,1969

3. A new model for initiation and growth of fatigue cracks;Lynch;Metal Science,1975

4. An engineering model for prediction of rolling contact fatigue of railway wheels;Ekberg;Fatigue Fract Eng Mater Struct,2002

5. On the Dang Van fatigue limit in rolling contact fatigue;Ciavarella;Int J Fatigue,2006

Cited by 53 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Reliability assessment under continuous fatigue degradation and shock based on Markov renewal process;Reliability Engineering & System Safety;2024-08

2. Retraction notice to “Reliability analysis of fatigue crack growth for rail steel under variable amplitude service loading conditions and wear” [Int. J. Fatigue 152 (2021) 106450];International Journal of Fatigue;2024-06

3. Reliability analysis of fatigue crack growth in shallow shell structures using the Dual Boundary Element Method;Theoretical and Applied Fracture Mechanics;2024-06

4. Failure mechanism and damage tolerance of turnout point rail in high-speed railway;Engineering Failure Analysis;2024-03

5. Research on Residual Life Prediction Method of Composites Based on Equivalent Number of Cycles Conversion;Journal of Failure Analysis and Prevention;2024-02-21

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线，采集、加工和组织学术论文而形成的新型学术文献查询和分析系统，可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容，当前同舟云学术共收录了国内外主流学术期刊6万余种，收集的期刊论文及会议论文总量共计约1.5亿篇，并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询！咨询电话：010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号京ICP备18003416号-3