Mode II fatigue delamination resistance of advanced fiber-reinforced polymer–matrix laminates: Towards the development of a standardized test procedure-Reference-Cited by-同舟云学术

Mode II fatigue delamination resistance of advanced fiber-reinforced polymer–matrix laminates: Towards the development of a standardized test procedure

Published:2013-05 Issue: Volume:50 Page:57-62
ISSN:0142-1123
Container-title:International Journal of Fatigue
language:en
Short-container-title:International Journal of Fatigue

Author:

Brunner A.J.,Stelzer S.,Pinter G.,Terrasi G.P.

Publisher

Elsevier BV

Subject

Industrial and Manufacturing Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,Modelling and Simulation

Reference32 articles.

1. Micromechanisms of interlaminar fracture and fatigue;Russell;Polym Compos,1987

2. Monitoring progression of mode-II delamination during fatigue loading through acoustic-emission in laminated glass–fiber composite;Roy;Polym Compos,1988

3. Mode II cyclic delamination growth;Threthewey;J Compos Mater,1988

4. Characterization of mode I and mode II delamination growth and thresholds in AS4/PEEK composites;Martin,1990

5. Thermal-damage effects on mode-II interlaminar fatigue crack propagation of graphite epoxy composites;Hwang;Compos Struct,1994

Cited by 42 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. A fatigue test based on inclined loading block concept to benchmark delamination growth considering loading history and R-curve effect;Composites Part A: Applied Science and Manufacturing;2024-06

2. Fatigue crack growth characterization of composite-to-steel bonded interface using ENF and 4ENF tests;Composite Structures;2024-04

3. Fatigue Testing and Modeling of Bonded Composite Specimens in Mode I, II, and Mixed-Mode I/II Loadings;Materials Performance and Characterization;2024-02-06

4. Mode I Fatigue of Fibre Reinforced Polymeric Composites: A Review;Polymers;2022-10-27

5. Mode II fatigue delamination behaviour of composite multidirectional laminates and the stress ratio effect;Engineering Fracture Mechanics;2022-04