Effect of microstructural aspects in the heat-affected zone of high strength pipeline steels on the stress corrosion cracking mechanism: Part I. In acidic soil environment-Reference-Cited by-同舟云学术

Effect of microstructural aspects in the heat-affected zone of high strength pipeline steels on the stress corrosion cracking mechanism: Part I. In acidic soil environment

Published:2019-11 Issue: Volume:160 Page:108167
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Li Xueda,Liu Jiahang,Sun Jianbo,Lin Xueqiang,Li Chunyu,Cao Ning

Funder

National Natural Science Foundation of China

Shandong Provincial Natural Science Foundation, China

Postdoctoral Innovation Project of Shandong Province

Fundamental Research Funds for the Central Universities

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference32 articles.

1. Heat affected zone microstructures and their influence on toughness in two microalloyed HSLA steels;Hutchinson;Acta Mater.,2015

2. Investigation on the microstructure and toughness of coarse grained heat affected zone in X-100 multi-phase pipeline steel with high Nb content;You;Mater. Sci. Eng. A,2012

3. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: discontinuous crack growth mechanism;Egbewande;Corros. Sci.,2014

4. Stress Corrosion Cracking: Theory and Practice;Raja,2011

5. Stress corrosion cracking of carbon steel in carbonate solutions;Sutcliffe;Corrosion,1972

Cited by 39 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Investigation of hydrogen embrittlement sensitivity of X65 pipeline steel with different compositions employing thermal simulation;International Journal of Hydrogen Energy;2024-09

2. Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials;Materials;2024-07-14

3. Investigating the hydrogen diffusion and cracking susceptibility of pipeline steels after various heat treatments;Engineering Failure Analysis;2024-07

4. Effect of tempering temperature on stress corrosion resistance of a low alloy high strength steel with high vanadium content;Materials Today Communications;2024-06

5. Effects of acicular ferrites on crystallography and incomplete transformation of low-carbon low-alloy steel;Journal of Materials Research and Technology;2024-05