Aging of polymeric composite specimens for 5000 hours at elevated pressure and temperature

Published:2001-01 Issue:1 Volume:61 Page:75-86
ISSN:0266-3538
Container-title:Composites Science and Technology
language:en
Short-container-title:Composites Science and Technology

Author:

Tsotsis Thomas K,Keller Scott,Lee Kyejune,Bardis Jason,Bish Jack

Publisher

Elsevier BV

Subject

General Engineering,Ceramics and Composites

Reference12 articles.

1. Tsotsis TK, Keller S, Lee K, Bardis J, Bish J. 3000 hours aging of polymeric composite specimens under elevated pressure and temperature. Presented at 44th International SAMPE Symposium, 24–27 Ma, 1999 (closed paper).

2. Preliminary examination of the use of elevated pressure to accelerate thermo-oxidative aging in composites;Tsotsis;Polym. Degrad. Stab.,1999

3. Thermo-oxidative aging of composite materials;Tsotsis;J. Comp. Mat.,1995

4. Long-term thermo-oxidative aging of composite materials: experimental methods;Tsotsis;J. Comp. Mat.,1998

5. Long-term thermo-oxidative aging of composite materials: failure mechanisms;Tsotsis;Comp. Sci. Tech.,1998

Cited by 94 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Accelerated oxidation of epoxy thermosets with increased O2 pressure;Polymer Degradation and Stability;2024-10

2. Microscopic and spectroscopic analysis of aged polymer composites;Aging and Durability of FRP Composites and Nanocomposites;2024

3. Effect of high-temperature thermo-oxidation on the mechanical and electrical properties of phenylethynyl-terminated polyimide/carbon fiber composite;Polymer Degradation and Stability;2023-12

4. Compressive anisotropy effects and crack evolution mechanisms of 3D5d braided composites induced by thermo-oxidative ageing;Composites Science and Technology;2023-07

5. Strain rate effect on compressive damages of thermo-oxidative aged 3D braided composites;Engineering Fracture Mechanics;2022-12