The relationship between pure delamination modes I and II on the crack growth rate process in cracked lap shear specimen (CLS) of 5 harness satin composites-Reference-Cited by-同舟云学术

The relationship between pure delamination modes I and II on the crack growth rate process in cracked lap shear specimen (CLS) of 5 harness satin composites

Published:2015-11 Issue: Volume:78 Page:350-357
ISSN:1359-835X
Container-title:Composites Part A: Applied Science and Manufacturing
language:en
Short-container-title:Composites Part A: Applied Science and Manufacturing

Author:

Shiino M.Y.,Alderliesten R.C.,Donadon M.V.,Cioffi M.O.H.

Funder

FAPESP

Publisher

Elsevier BV

Subject

Mechanics of Materials,Ceramics and Composites

Reference32 articles.

1. Fatigue crack constrain in plain-woven CFRP using newly-developed spread tows;Nishikawa;Int J Fatigue,2006

2. Damage development in woven fabric composites during tension–tension fatigue;Hansen;J Compos Mater,1999

3. Shiino MY, Alderliesten RC, Donadon MV, Voorwald HJC, Cioffi MOH. Applicability of standard delamination tests (double cantilever beam and end notch flexure) for 5HS fabric-reinforced composites en weft-dominated surface. J Compos Mater. http://dx.doi.org/10.1177/0021998314549821.

4. The effect of weave pattern and crack propagation direction on mode I delamination resistance of woven and carbon composites;Alif;Composites Part B,1998

5. Fatigue crack growth rate in mode I of a carbon fiber 5HS weave composite laminate via RTM;Shiino;Adv Mater Res,2014

Cited by 6 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Numerical Modelling and Validation of Mixed-Mode Fracture Tests to Adhesive Joints Using J-Integral Concepts;Processes;2022-12-17

2. Prediction of laminate delamination from strength failure of interlaminar matrix-layer;Journal of Reinforced Plastics and Composites;2022-05-26

3. Mode II delamination of carbon-glass fiber/epoxy hybrid composite under fatigue loading;International Journal of Fatigue;2022-01

4. Mode I and mode II delamination of carbon/glass/epoxy hybrid composite: A statistics‐based analysis;Polymer Composites;2021-05

5. Hygrothermal Effect on Composites Under In-Plane Fatigue at Stress Ratios of R = −1 and R = 0.1: An Analysis of Quasi-Isotropic Stitched Carbon Fibers;Journal of Materials Engineering and Performance;2018-10-10