Author:
Potekaev A.I.,Chaplyginа A.A.,Starostenkov M.D.,Klopotov A.A.,Kulagina V.V.
Abstract
The analysis of the atomic and phase structure confirmed the difference between the structural-phase states at the heating and cooling stages. Based on the analysis of the influence of the deviation of the atomic composition from the stoichiometric condition of the intermetallic compound during cooling, it is established that the deviation is a significant factor in the area of low-stability pre-transitional structural-phase states before the transformation. The behavior of the long-range parameter temperature dependence curves during the cooling of alloys of non-stoichiometric compositions differs significantly from the behavior of the corresponding alloy curve of a stoichiometric composition alloy. It is shown that in the case of cooling of alloys of non-stoichiometric compositions, a significant supercooling is required to establish a long-range order, and the appearance of ordered phases occurs at significantly lower temperatures. It is found that the temperature dependence curve of the long-range parameter of the Ni45Al55 alloy is significantly lower than the corresponding curve of the Ni55Al45 alloy. This indicates different mechanisms for establishing the long-range order of alloys with non-stoichiometric compositions. It is noted that the deviation of the system composition from the stoichiometric one causes a significant reduction of ordered and disordered regions. This article is a continuation of the work published earlier in the journal Izvestiya AltGU. 2020. №1 (111).
Reference20 articles.
1. Li H., Qiao M., Zhou C.G. Formation and cyclic oxidation resistance of Hf-Co-modified aluminide coatings on nickel base superalloys // Materials Chemistry and Physics. 2014. Vol. 143.
2. Sun F., Mao S.C., Zhang J.X. Identification of the par-titioning characteristics of refractory elements in a and у phases of Ni-based single crystal superalloys based on first principles // Materials Chemistry and Physics. 2014. Vol. 147.
3. Козлов Э.В., Клопотов А.А., Тайлашев А.С., Солоницина Н.О. Система Ni-Al. Кристаллогеометрические особенности // Известия РАН. Сер. Физ. 2006. Т. 70, №7.
4. Kazimirov V.P., Roik A.S., Samsonnikov A.V. et al. Pattern of the Atom Ordering in a Melt and Surface Properties of Systems with Intermetallic Compounds // Journal of Super-hard Materials. 2009. Vol. 31. No. 4.
5. Мурин А.В., Шабанова И.Н. Моделирование локальной кластерной структуры двухкомпонентной системы AlNi в жидком и переохлажденном состоянии // Химическая физика и мезоскопия. 2016. Т. 18.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献