Qi Zhi-Jian ,Huang Wei-Gang ,
Abstract
A novel Ca3Si3O9:Dy3+ phosphor for white LED was prepared by sol-gel method. The structure and luminescent properties of Ca3Si3O9:Dy3+ phosphors with different concentration of Dy3+ and charge compensator Li+ were characterized by X-ray diffraction (XRD) and photoluminescence (PL) spectra. Results show that the emission spectrum consists of two main band peaks locatied at 483 nm and 577 nm, while the peaks of excitation spectrum are located in the rang of 290–480 nm. Both of luminescent intensity and the ratio of yellow to blue emission (Y/B) increase first and then decrease with increasing Dy3+ concentration; and the luminescent intensity reaches a maximum when Dy3+ concentration is of 1 mol%. The luminescent intensity of Ca3Si3O9:Dy3+can be enhanced by Li+, and the blue emission increases greatly when Li+ concentration is within the range of 2 to 4 mol%.
Publisher
Acta Physica Sinica, Chinese Physical Society and Institute of Physics, Chinese Academy of Sciences
Subject
General Physics and Astronomy
Reference14 articles.
1. Li P L, Yang Z P, Wang Z J, Guo Q L 2008 Chin. Phys. B 17 1135
2. Nishiura S, Tanabe S, Fujioka K, Fujimoto Y 2011 Opt. Mater. 33 688
3. Zhang X H, Lu Z M, Meng F B, Lu F, Hu L, Xu X W, Tang C C 2012 Mater. Lett. 66 16
4. Lei F, Yan B 2008 J. Solid State Chem. 181 855
5. Luo Y Y, Jo D S, Senthil K, Tezuka S, Kakihana M, Toda K, Masaki T, Yoon D H 2012 J. Solid State Chem. 189 68
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献