Abstract
In the absence of a corrosive environment, brittle materials such as silicon should be immune to cyclic fatigue. However, fatigue effects are well known in micrometer-sized polycrystalline silicon (polysilicon) samples tested in air. To investigate the origins of this phenomenon in polysilicon, we developed a fixed-grip fracture mechanics microspecimen but could find no evidence of static stress corrosion cracking. The environmental sensitivity of the fatigue resistance was also investigated under cyclic loading. For low-cycle fatigue, the behavior is independent of the ambient conditions, whether air or vacuum, but is strongly influenced by the ratio of compressive to tensile stresses experienced during each cycle. The fatigue damage most likely originates from contact stresses at processing-related surface asperities; subcritical crack growth then ensues during further cyclic loading. The lower far-field stresses involved in high-cycle fatigue induce reduced levels of fatigue damage. Under these conditions, a corrosive ambient such as laboratory air exacerbates the fatigue process. Without cyclic loading, polysilicon does not undergo stress corrosion cracking.
Publisher
American Association for the Advancement of Science (AAAS)
Reference32 articles.
1. Crystal Structures at High Pressures of Metallic Modifications of Silicon and Germanium
2. Stress corrosion cracking (sometimes called “static fatigue” in the ceramics literature) is the propagation of a sharp crack in a brittle solid under an applied stress too low for catastrophic fracture and in the presence of a corrosive environment. In the case of silica glass for which the existence of stress corrosion in the presence of humidity is well established the ambient H 2 O molecules react with crack-bridging Si-O-Si bonds and create two Si-O-H surface groups with localized crack extension ( 27 ).
3. Fitzgerald A. M., Iyer R. S., Dauskardt R. H., Kenny T. W., J. Mater. Res. 17, 683 (2002).
4. Slow Crack Growth in Single-Crystal Silicon
5. Van Arsdell W. W., Brown S. B., J. Microelectromech. Syst. 8, 319 (1999).