Abstract
Abstract
In this study, an environmentally friendly mesoporous material called COK-12 was created using inexpensive sodium silicate as a silica source and surfactant P123 as a soft template. COK-12 was then modified with p-xylene to produce a template called P-COK-12, which had a compact and well-ordered pore structure. For the first time, this modified mesoporous material was used as a template to prepare a mesoporous La0.8Sr0.2MnO3 (LSM) catalyst through a combination of the nano-casting and sol-gel methods. The results showed that the LSM-550 catalyst, synthesized at 550 °C for 2 hours, had a large specific surface area of 72.11 m2/g and the highest molar ratio of surface Mn4+/Mn3+ and Oads/Olat. Additionally, the CO conversion results for different LSM-T samples (T=550, 600, 650, 700 °C) indicated that the LSM-550 sample exhibited the best catalytic activity, with T50 of 180 °C and T90 of 218 °C, as well as excellent stability.
Publisher
Research Square Platform LLC
Reference26 articles.
1. Pahalagedara L, A.Kriz D, Wasalathanthri N, Weerakkody C, Meng YT, Dissanayake S, Pahalagedara M, Luo Z, L.Suib S, Nandi P, J.Meyer R (2017) Appl Catal B 204:411–420
2. Pilger F, Testino A, Lucchini MA, Kambolis A, Tarik M, Kazzi ME, Arroyo Y, Rossell MD, Ludwig C, Nanosci J (2015) Nanotechnol 15:3530–3539
3. Rodriguez JA, Si R, Evans J, Xu W, Hanson JC, Tao J, Zhu Y (2015) Catal Today 240:229–235
4. Tarjomannejad A, Farzi A, Gómez MJI, Niaei A, Salari D, Albaladejo-Fuentes V (2016) Catal Lett 146:2330–2340
5. Xiao P, Zhu J, Li H, Jiang W, Wang T, Zhu Y, Zhao Y, Li J (2014) ChemCatChem 6:1774–1781