Study on the effect of heat treatment on the structure, mechanical and electrical properties of alumina fiber insulation

Abstract

Abstract In this paper, the heat treatment of alumina fiber was studied. The infiltration agent on the fiber surface was removed after heat treatment at 450 °C for 6 h. TG-DSC, scanning electron microscope, x-ray diffraction, Fourier infrared spectrometer, energy dispersive spectrometer, and patterning were used to analyze the thermal weight loss, fiber surface morphology, crystal structure, and composition of alumina fibers. The results show that the aluminum oxide fiber has excellent temperature resistance and does not undergo crystal phase transformation during thermal weight loss. After heat treatment, the fiber surface infiltration agent ablates and dissolves from the fiber surface, and the internal crystal structure of the fiber remains stable. The tensile testing machine was utilized to test the breaking strength of alumina fiber. The fiber still maintained high strength after heat treatment, and the retention rate of breaking strength was greater than 74%. ZC-90G high insulation resistance measuring instrument and WDY-Ⅱ automatic voltage tester were utilized to analyze the insulation resistivity and breakdown strength of alumina fiber before and after heat treatment. The results show that heat treatment can effectively improve the insulation performance and breakdown strength of alumina fiber.