Abstract
Abstract
We have studied the capability of He+ focused ion beam (He+-FIB) patterning to fabricate defect arrays on the Si/SiO2/Graphene interface using a combination of atomic force microscopy (AFM) and Raman imaging to probe damage zones. In general, an amorphized ‘blister’ region of cylindrical symmetry results upon exposing the surface to the stationary focused He+ beam. The topography of the amorphized region depends strongly on the ion dose, DS
, (ranging from 103 to 107ions/spot) with craters and holes observed at higher doses. Furthermore, the surface morphology depends on the distance between adjacent irradiated spots, LS
. Increasing the dose leads to (enhanced) subsurface amorphization and a local height increase relative to the unexposed regions. At the highest areal ion dose, the average height of a patterned area also increases as ∼1/LS
. Correspondingly, in optical micrographs, the µm2-sized patterned surface regions change appearance. These phenomena can be explained by implantation of the He+ ions into the subsurface layers, formation of helium nanobubbles, expansion and modification of the dielectric constant of the patterned material. The corresponding modifications of the terminating graphene monolayer have been monitored by micro Raman imaging. At low ion doses, DS
, the graphene becomes modified by carbon atom defects which perturb the 2D lattice (as indicated by increasing D/G Raman mode ratio). Additional x-ray photoionization spectroscopy (XPS) measurements allow us to infer that for moderate ion doses, scattering of He+ ions by the subsurface results in the oxidation of the graphene network. For largest doses and smallest LS
values, the He+ beam activates extensive Si/SiO2/C bond rearrangement and a multicomponent material possibly comprising SiC and silicon oxycarbides, SiOC, is observed. We also infer parameter ranges for He+-FIB patterning defect arrays of potential use for pinning transition metal nanoparticles in model studies of heterogeneous catalysis.
Funder
German Research Foundation DFG under the Cluster of Excellence “e-conversion”
Helmholtz Association under the POF-3 Programme “Science and Technology of Nanosystems (STN)”
Young Academy of the Bavarian Academy of Sciences and Humanities.
Subject
Electrical and Electronic Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,General Chemistry,Bioengineering
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献