Rapid low-temperature densification of Ag2Se bulk material: mass transfer through the dissociative adsorption reaction of Ag protrusions and Se saturated vapor

Abstract

Abstract In materials science, the impact of density on a material’s capabilities is profound. Conventional sintering requires high temperatures and is energy-demanding, propelling the pursuit of less intensive, low-temperature densification methods. Electric field-assisted sintering has recently gained attention for its simplicity and effectiveness, offering a new frontier in low-temperature densification. In this study, dense bulk materials were produced by subjecting monophasic Ag2Se powders to electric field-assisted sintering, where a direct current with an average value of 4 A was applied, achieving a peak temperature of 344 K. The novel low-temperature densification mechanism unfolds thus: nanoscale silver protrusions, stimulated by electrical current, engage in a dissociative adsorption reaction with the ambient saturated selenium vapor. This process swiftly engenders the formation of fresh silver selenide (Ag2Se) compounds, initiating nucleation and subsequent growth. Consecutively, these compounds seamlessly occupy and expand, perpetually bridging the interstices amidst the powders. In a scant 8 s, the density swiftly surpassed 99%, yielding a bulk material that exhibited a ZT value of 1.07 at 390 K. This investigation not only attains an unparalleled density at low temperatures but also charts a pioneering course for material densification in such conditions.