Abstract
Abstract
Studying the mechanical properties of aluminum alloy 6061 friction stir welded (FSW) joints after ultrasonic peening treatment (UPT) under very high cycle fatigue (VHCF) loading. The effect of joints ultrasonic peening treatment was explored. It can be seen from the results that the ultrasonic peening treatment can form a reinforced layer on the surface of joints, and the fatigue crack source is transferred from the surface of the specimen to the inside. However, the change of fatigue crack initiation site does not improve the fatigue strength of specimen through ultrasonic peening treatment. The fatigue strength of the aluminum alloy 6061 joint after ultrasonic peening treatment is even lower than as a received condition. The characteristics of fatigue crack initiation and the mechanism of surface strengthened layer on fatigue strength were analyzed and discussed.
Reference12 articles.
1. Strengthening Steel Components by Ultrasonically Vibrating Ball[J];Mukhanov,1966
2. Mechanical properties of friction stir welds in thin sheet of aluminium 2024, 6013 and 7475[A];Magnusson,2000
3. The role of residual stress and heat affected zone properties on fatigue crack propagation in friction stir welded 2024-T351 aluminium joints[J];Bussu;International Journal of Fatigue,2003
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献