Abstract
Abstract
Study about Influence of Dy-doping in Nd2Fe14B on its structural and magnetic properties have been performed. The combination of Nd2-xDyxFe14B with x= 0.00, 0.33, 0.67, and 1.00 were using the conventional method of arc melting. The result of ingot then milled and compacted to produce a permanent magnet sample. The results of phase analysis with XRD show that the sample contained 3 phases, namely Nd2Fe14B, Fe, and Nd with dominant phase above 50% is Nd2Fe14B. Magnetic properties was measured using permeagraph and produce saturation magnetization of 0.6, 0.56, 0.42, and 0.4, remanent of 0.15, 0.19, 0.26, and 0.25, and coersivitas field of 0.35, 0.39, 3.0, and 1.29 kOe for composition of 0, 0.33, 0.67, and 1, respectively. The remanent magnetization ratio toward saturation of Br/Bs of this increase significantly from 0.34 to 0.62 for the composition x= 0.67, and has the highest energy product of 0.195 MGOe. To determine the effect of Dy substitution towards micro structure was observed with an optical microscope. It was concluded that the effect of Dy substitution towards optimum magnetic behavior was found in the composition x= 0.67.
Subject
General Physics and Astronomy
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献