Biofabrication approaches toward the development of tissue-engineered vascular grafts (TEVGs) have been widely investigated. However, successful translation has been limited to large diameter applications, with small diameter grafts frequently failing due to poor mechanical performance, in particular mismatched radial compliance. Herein, melt electrowriting (MEW) of poly(ϵ-caprolactone) has enabled the manufacture of highly porous, biocompatible microfibre scaffolds with physiological anisotropic mechanical properties, as substrates for the biofabrication of small diameter TEVGs. Highly reproducible scaffolds with internal diameter of 4.0 mm were designed with 500 and 250 µm pore sizes, demonstrating minimal deviation of less than 4% from the intended architecture, with consistent fibre diameter of 15 ± 2 µm across groups. Scaffolds were designed with straight or sinusoidal circumferential microfibre architecture respectively, to investigate the influence of biomimetic fibre straightening on radial compliance. The results demonstrate that scaffolds with wave-like circumferential microfibre laydown patterns mimicking the architectural arrangement of collagen fibres in arteries, exhibit physiological compliance (12.9 ± 0.6% per 100 mmHg), while equivalent control geometries with straight fibres exhibit significantly reduced compliance (5.5 ± 0.1% per 100 mmHg). Further mechanical characterisation revealed the sinusoidal scaffolds designed with 250 µm pores exhibited physiologically relevant burst pressures of 1078 ± 236 mmHg, compared to 631 ± 105 mmHg for corresponding 500 µm controls. Similar trends were observed for strength and failure, indicating enhanced mechanical performance of scaffolds with reduced pore spacing. Preliminary in vitro culture of human mesenchymal stem cells validated the MEW scaffolds as suitable substrates for cellular growth and proliferation, with high cell viability (>90%) and coverage (>85%), with subsequent seeding of vascular endothelial cells indicating successful attachment and preliminary endothelialisation of tissue-cultured constructs. These findings support further investigation into long-term tissue culture methodologies for enhanced production of vascular extracellular matrix components, toward the development of the next generation of small diameter TEVGs.
Funder
Metro North Hospital and Health Service
Queensland University of Technology
Subject
Biomedical Engineering,General Medicine,Biomaterials,Biochemistry,Bioengineering,Biotechnology
Reference55 articles.
1. The top 10 causes of death;World Health Organization,2020
2. Development of tissue engineered vascular grafts and application of nanomedicine;Rathore;Wiley Interdiscip. Rev. Nanomed. Nanobiotech.,2012
3. Bioprinting small diameter blood vessel constructs with an endothelial and smooth muscle cell bilayer in a single step;Xu;Biofabrication,2020
4. Vascular prostheses;The British Standards Institution, Cardiovascular implants and extracorporeal systems,2017
5. Indirect burst pressure measurements for the mechanical assessment of biological vessels;Geelhoed;Tissue Eng. C,2019
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献