7075 aluminum alloy butt welding was carried out by TIG welding with self-made 7075 wire. The effects of different currents on the microstructure and mechanical properties of the joint before and after heat treatment were studied. Before heat treatment, the strength and elongation of the joint are 274.84 MPa and 6.3%, which are determined by the presence of a large number of second phase precipitates with different shapes. After heat treatment, the tensile strength and elongation are increased to 511.75 MPa and 13.76%. Since most of the second phase has been dissolved, the grain size becomes the decisive factor. The fine grain size and more sufficient recrystallization degree make the mechanical properties of the low-current joint better.
Funder
National Natural Science Foundation of China
Subject
Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials
Reference23 articles.
1. Transmission electron microscopy investigation of separated nucleation and in situ nucleation in AA7050 aluminium alloy;Chung;Acta Mater.,2018
2. Recent advances in the development of aerospace materials;Zhang;Prog. Aerosp. Sci.,2018
3. Application of modern aluminum alloys to aircraft;Staley;Prog. Aerosp. Sci.,1996
4. Porosity, element loss, and strength model on softening behavior of hybrid laser arc welded Al-Zn-Mg-Cu alloy with synchrotron radiation analysis;Wu;Welding Journal,2013
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献