Abstract
Abstract
With an increase in the annealing temperature, the hydrothermally synthesized BaTiO3 nanopowders increased in particle sizes from 100 to 260 nm and decreased in pore volume from 7.2 to 2.82 cm3 g−1, while the pore size remained constant at 3.06 nm. Samples with different initial particle sizes were sintered in the temperature range of 1210 °C–1300 °C and for periods of 0.5–48 h at 1270 °C. The kinetic grain-growth exponent of the sintered BaTiO3 samples, n, was proportional to the increase of an initial particle size and the decrease of pore volume, and the grain growth obeyed the Arrhenius equation. The activation energies for the grain growth of the sintered BaTiO3 samples with initial particle size of 100, 155 and 260 nm were 737, 702 and 755 kJ mol−1, respectively, indicating that the activation energy was independent of the initial particle size in the range of 100–300 nm under identical purity conditions, and pore volume was supposed to be attributed to the velocity of grain growth.
Funder
Ministry of Trade, Industry & Energy
Subject
Metals and Alloys,Polymers and Plastics,Surfaces, Coatings and Films,Biomaterials,Electronic, Optical and Magnetic Materials
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献