Corrosion behavior of carbon steel in H2S-CO2-H2O-methyldiethanolamine (MDEA) solution under the presence of chloride ions

Abstract

Purpose This paper aims to study the effect of chloride ions concentration on the corrosion behavior of carbon steel in methyldiethanolamine (MDEA) aqueous solution in the sight of different process parameters of purification plant. Design/methodology/approach Due to the decrease of filtration efficiency and separation efficiency, the chloride ion in the desulfurization solution is enriched. The corrosion behavior of carbon steel under chloride ion enrichment environment was studied by weight-loss method, electrochemical impedance spectroscopy, cyclic polarization curve, X-ray photoelectron spectroscopy and scanning electron microscopy. Findings The results show that temperature and hydrogen sulfide loads are the main factors of corrosion in CO2-MDEA-H2O-H2S environment. The enrichment of chloride ions reduces the corrosion rate at low temperature but promotes the corrosion rate at high temperature. The chloride concentration should be controlled below 3000 mg/L, and no pitting corrosion was found under the experimental conditions. Originality/value The effect of chloride ion enrichment on MDEA solution corrosion shows that at low temperature, the increase of chloride ion will reduce the acid gas load and increase the density of corrosion products, so as to reduce the corrosion; on the contrary, at high temperature, the density of corrosion products will decrease and the corrosion will be intensified as well. It is believed that the chloride ion should be controlled below 3000 mg/L according to the results of the tests.