An Qi,Samwer Konrad,Demetriou Marios D.,Floyd Michael C.,Duggins Danielle O.,Johnson William L.,Goddard William A.
Abstract
To gain insight into the large toughness variability observed between metallic glasses (MGs), we examine the origin of fracture toughness through bending experiments and molecular dynamics (MD) simulations for two binary MGs: Pd82Si18 and Cu46Zr54. The bending experiments show that Pd82Si18 is considerably tougher than Cu46Zr54, and the higher toughness of Pd82Si18 is attributed to an ability to deform plastically in the absence of crack nucleation through cavitation. The MD simulations study the initial stages of cavitation in both materials and extract the critical factors controlling cavitation. We find that for the tougher Pd82Si18, cavitation is governed by chemical inhomogeneity in addition to topological structures. In contrast, no such chemical correlations are observed in the more brittle Cu46Zr54, where topological low coordination number polyhedra are still observed around the critical cavity. As such, chemical inhomogeneity leads to more difficult cavitation initiation in Pd82Si18 than in Cu46Zr54, leading to a higher toughness. The absence of chemical separation during cavitation initiation in Cu46Zr54 decreases the energy barrier for a cavitation event, leading to lower toughness.
Funder
DOD | Defense Advanced Research Projects Agency
DOD | U.S. Army | AMC | U.S. Army Research Laboratory
NSF | MPS | Division of Materials Research
Publisher
Proceedings of the National Academy of Sciences
Cited by
42 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献