The effect of M (M = Ce, Zr, Ce–Zr) on rolling microstructure and mechanical properties of FH40

Abstract

AbstractCe, Zr and Ce–Zr composite experimentl steel were prepared by vacuum induction furnace and 550 twin-roll reversible rolling mill. Optical microscope (OM), scanning electronic microscopy (SEM) and energy dispersive spectrometer (EDS) were used to observe the rolling microstructure of the experimental steel. The mechanical properties of the experimental steel were tested and analyzed. The effect of cerium zirconium oxide inclusions on nucleation, tensile and impact fracture mechanism of intragranular acicular ferrite (IAF) was investigated. The results show that the rolling microstructure of steel containing 0.0052% Ce and the steel under composite treatment containing 0.0053% Ce and 0.0055% Zr is refined. IAF generation can be induced by Al–Ce–O inclusion of the size of 4 µm or induced by Al–Ce–Zr–O + MnS inclusion of the size of 3 µm. The yield strength and tensile strength of the steel treated by Ce–Zr are 428 and 590 MPa, respectively, the elongation is 23.55%, the longitudinal impact energy at −60°C is 189 J, which are 31, 45, 46 J and 6.25%, respectively, higher than those of the matrix steel. The dimple of the experimental steel at the fracture surface is larger and deeper than that of the matrix steel. The small inclusions in uniform distribution contribute to the high tensile strength of the experimental steel.