Failure investigation of a spline half-shaft in a loader rickshaw differential system

Author:

Hayat Umer1ORCID,Shad Muhammad Rizwan1,Ali Ahmad1,Abbas Hassan1,Hassnain Muhammad1

Affiliation:

1. Mechanical Engineering Department , University of Central Punjab , Lahore , Pakistan

Abstract

Abstract Large number of pre-mature failure cases of spline half-shafts of loader automobile rickshaws were encountered by an industry in Lahore, Pakistan. Unexpected fracture of the spline-region of half-shafts were reported shortly after the shafts were put to service. This paper presents the findings of a systematic investigation that was carried out to find the root cause of the failure. Visual inspection, mechanical characterization, microstructural analysis, and chemical composition analysis were used to study the failure. It was revealed that the failure was torsional fatigue fracture in nature, with crack initiating from one of the machining marks present near the spline-root. Main cause of failure was found to be stress concentration at machine marks present on the surface, especially the ones closer to spline-roots, resulting in crack initiation. Moreover, other factors like presence of manganese sulfide (MnS) inclusions and improper material had also contributed towards crack propagation and final fracture.

Publisher

Walter de Gruyter GmbH

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3