Research on Optimization of Process Parameters of Electroless Nickel Plating Based on Orthogonal Test

Published:2022-07-11 Issue:1(17) Volume: Page:97-102
ISSN:2410-485X
Container-title:Grand Altai Research & Education / Наука и образование Большого Алтая
language:ru
Short-container-title:

Author:

Zhou C.,Chai X.,Mei S.,Burial L.

Abstract

As a widely used surface strengthening technology, electroless plating can be applied to various materials such as metals and non-metals, but its process parameters are numerous and difficult to optimize. For this reason, this study designed a three-factor and four-level orthogonal experimental scheme with the main salt/reducing agent molar ratio, lactic acid and PH value as the factors, and the plating speed and microhardness as the evaluation indicators. The range analysis was carried out on the experimental results, the best process parameters were selected, and the influence rules and reasons of the three factors on the evaluation indexes were discussed.

Publisher

Altai State Technical University

Reference12 articles.

1. Федюкин, В.К. Термоциклическая обработка металлов и деталей машин. В.К. Федюкин, М.Е. Смагоринский. Л.: Машиностроение. Ленинград. Отд., 1989. 255 с. @ 1. Fedyukin, V.K. Termociklicheskaya obrabotka metallov i detalej mashin. V.K. Fedyukin, M.E. Smagorinskij. L.: Mashinostroenie. Leningrad. Otd., 1989. 255 s.

2. Ворошнин, Л.Г. Борирование стали. Л.Г. Ворошнин, Ляхович Л.С. М.: Металлургия, 1978. 239 с. @ 2. Voroshnin, L.G. Borirovanie stali. L.G. Voroshnin, Lyahovich L.S. M.: Metallurgiya, 1978. 239 s.

3. Гурьев, А.М. Влияние состава насыщающей среды на структуру и свойства диффузионного слоя при титанировании сталей. А.М. Гурьев, Б.Д. Лыгденов // Изв. Вузов. Физика. №11. 2000. Т. 43. С. 269-270. @ 3. Gur'ev, A.M. Vliyanie sostava nasyshchayushchej sredy na strukturu i svojstva diffuzionnogo sloya pri titanirovanii stalej. A.M. Gur'ev, B.D. Lygdenov // Izv. Vuzov. Fizika. №11. 2000. T. 43. S. 269-270.

4. Гурьев, А.М. Физические основы химико-термоциклической обработки сталей. А.М. Гурьев, Б.Д. Лыгденов, Н.А. Попова, Э.В. Козлов. Барнаул, 2008. @ 4. Gur'ev, A.M. Fizicheskie osnovy himiko-termociklicheskoj obrabotki stalej. A.M. Gur'ev, B.D. Lygdenov, N.A. Popova, E.V. Kozlov. Barnaul, 2008.

5. Лыгденов, Б.Д. Интенсификация процессов формирования структуры диффузионного слоя при химико-термической обработке сталей Б.Д. Лыгденов / диссертация на соискание ученой степени доктора технических наук / ГОУВПО «Алтайский государственный технический университет». Барнаул, 2009. @ 5. Lygdenov, B.D. Intensifikaciya processov formirovaniya struktury diffuzionnogo sloya pri himiko-termicheskoj obrabotke stalej B.D. Lygdenov / dissertaciya na soiskanie uchenoj stepeni doktora tekhnicheskih nauk / GOUVPO «Altajskij gosudarstvennyj tekhnicheskij universitet». Barnaul, 2009.