Abstract
AbstractThis paper examined the cyclic deformation behaviour of multiphase low-carbon steel that was subjected to austempering heat treatments at four temperatures (190 °C, 230 °C, 275 °C, and 315 °C) below the martensite start temperature (Ms = 353 °C). The tests were conducted at room temperature, under fully reversed strain-controlled conditions, with strain amplitudes in the range 0.5–1.0%. The microstructure was observed by transmission electron microscopy, and the fracture surfaces were examined by scanning electron microscopy. The steel had a bainite/martensite microstructure, with increasing bainite content for higher austempering temperatures. Irrespective of the tested conditions, it strain-hardened during the first two cycles and then, strain-softened until failure. The austempering temperature did not significantly affect the stress-based, strain-based and energy-based relationships. However, lower austempering temperatures slightly improved the fatigue performance.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Civil and Structural Engineering
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献