Investigation of Probable Cause of Premature Cracking of Downcomer Nozzle of Heat Recovery Steam Generator-Reference-Cited by-同舟云学术

Investigation of Probable Cause of Premature Cracking of Downcomer Nozzle of Heat Recovery Steam Generator

Published:2009-10-07 Issue:6 Volume:9 Page:517-521
ISSN:1547-7029
Container-title:Journal of Failure Analysis and Prevention
language:en
Short-container-title:J Fail. Anal. and Preven.

Author:

Ghosh D.,Roy H.,Shukla A. K.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Safety, Risk, Reliability and Quality,General Materials Science

Link

http://link.springer.com/content/pdf/10.1007/s11668-009-9297-z.pdf

Reference5 articles.

1. British Electricity International: Modern Power Station Practice, Vol. B: Boilers and Ancillary Plants, 3rd edn. Elsevier, Amsterdam (1991)

2. Viswanathan, R., Foulds, J.R.: Service experience, structural integrity, severe accidents and erosion in nuclear and fossil plants. In: ASME Pressure Vessels and Piping Conference, vol. 303, pp. 187–205 (1995)

3. Saha, A., Roy, H., Ray, S., Maiti, M., Chowdhury, K.K., Shukla, A.K., Basu, J.: Investigation of probable cause of damage of steam drum of naphtha cracking furnace. Eng. Fail. Anal. 16(5), 1387–1396 (2009)

4. Viswanathan, R.: Damage Mechanisms and Life Assessment of High Temperature Components. ASM International, Metals Park, OH (1989)

5. Ellis, F.B.: Remaining life assessment of boiler pressure parts. Final report RP 22353-1, vols. 1–5. EPRI, Paolo Alto, CA (1988)

Cited by 9 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Defects as a root cause of fatigue failure of metallic components. II: Non-metallic inclusions;Engineering Failure Analysis;2019-04

2. Failure Analysis of PRDS Pipe in a Thermal Power Plant Boiler;Journal of The Institution of Engineers (India): Series C;2016-06-24

3. Investigation on Failure of a Drilling Rig Mast Structure;Journal of Failure Analysis and Prevention;2015-06-24

4. High-Temperature Graphitization Failure of Primary Superheater Tube;High Temperature Materials and Processes;2015-01-01

5. Metallurgical Failure Analysis of Drum Arching Tube of a 140 MW Thermal Power Plant;Journal of Failure Analysis and Prevention;2014-08-06